Preparation of thermosensitive silica by in situ one-pot method
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    采用原位一步法合成了温敏改性聚 N-异丙基丙烯酰胺(PNIPAAm)/SiO2纳米复合物. 通过接触角对温敏改性的纳米SiO2进行了条件优化:反应温度73℃,反应时间6 h,单体用量与KH-570摩尔比为1:1,引发剂用量为单体用量与KH-570总质量的2.5%。通过TEM、FT-IR、XPS等手段对温敏性纳米SiO2的组成和结构进行了表征。同时,这一有机-无机纳米复合物仍然保持PNIPAAm 的温度响应性, 最低临界溶解温度(LCST)与纯PNIPAAm相似。

    Abstract:

    A novel thermo-sensitive poly (N-isopropylacrylamide) (PNIPAAm)/ silica nano-composite has been prepared via in situ one-pot method . Effects of factors, such as reaction temperature, reaction time, monomer dosage and initiator dosage on the influence of contact angles were investigated. The optimum surface modification conditions were determined as: reaction temperature was 73℃, reaction time was 6 h, monomers and KH-570 molar ratios is 1, The amount of initiator monomer is 2.5 (wt%)of the total mass amount of monomer and KH-570. The samples were characterized by fourier transform infrared transmission emission microscope (TEM) and dynamic light scatter (DLS). Moreover, the thermo-sensitive property of PNIPAAm was retained in the nano-composite, which had a lower critical solution temperature similar to that of pure PNIPAAm.

    参考文献
    相似文献
    引证文献
引用本文

武江红.原位一步法制备温敏改性纳米二氧化硅[J].精细化工,2013,30(12):

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2012-11-21
  • 最后修改日期:2013-01-05
  • 录用日期:2013-01-08
  • 在线发布日期: 2013-10-30
  • 出版日期: